MECHANICAL PROPERTIES OF LAMINATE

Cured at 130 oC for 60 minutes and 3 bar

Flexural strength (Mpa): 850

Flexural modulus (Gpa): 54

Tensile strength (MPa): 550

Tensile modulus (GPa): 60

ILSS - Short Beam Shear (Mpa): 67

Tg (DSC) 20 oC / min: 128 oC

Linear weight: 34.52 g / m

Warp: 3K carbon fiber, 50%

Weft: 3K carbon fiber, 50%

Length, diameter and linear weight of braids vary greatly, depending on tension (stretch) applied. Technical data and price are given to the point where warp and weft are at the +- 45 degree angle (or vertical to each other).

Areal weight: 210 g / m2

Weaving style: Twill 2X2

Width: 1.20 meters

Warp: 3K TR30S carbon fiber + aram. 1260, 50%, 3.2+3.2=6,4 ends(threads) / cm

Weft: 3K TR30S carbon fiber + aram. 1260, 50%, 3.2+3.2=6,4 ends(threads) / cm

Fiber content by weight: 61% carbon / 39% aramid

MECHANICAL PROPERTIES OF FIBERS USED

Carbon:

Tensile strength (MPa): 4410

Tensile modulus (GPa): 235

Elongation at break (%): 1.9

Aramid:

Tensile strength (MPa): 2987

Tensile modulus (GPa): 91

Elongation at break (%): 3.10